Rhodium concentrate JE88-1 CLEAN - 1 g/100ml Rh
Product number:
8288.100
Product information "Rhodium concentrate JE88-1 CLEAN - 1 g/100ml Rh"
The rhodium concentrate JE88-1 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. The rhodium concentrate CLEAN is produced exclusively from recycled rhodium. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 0,5 µm can be deposited.
Operating data:
Rhodium content: 1,0 g/100ml Rh
pH-Value: <1
Operating conditions:
Voltage: 2-3 Volt
Bath temperature: 20-35°C
Exposition time: 2 min. (1-max. 10 min.)
Anodes: platinized titanium or mixed metal oxide
Anode/Cathode surface: 1 : 1
Agitation: advantageous
Current density: 0,5 - 2 A/dm2
Bath filtration: from 10 liters
Deposition data:
Hardness: 800 - 900 HV
Layer thickness: max. 0,5 µm
Layer density: approx. 12,4 g/cm3
Form of delivery:
-Ready for use 1 g/L Rh
-Concentrate form 1 g/100ml Rh for 1 litre bath
Concentrated bath preparation:
Mix 100 ml of the Rhodium JE88 concentrate with 900 ml distilled water.
Operating data:
Rhodium content: 1,0 g/100ml Rh
pH-Value: <1
Operating conditions:
Voltage: 2-3 Volt
Bath temperature: 20-35°C
Exposition time: 2 min. (1-max. 10 min.)
Anodes: platinized titanium or mixed metal oxide
Anode/Cathode surface: 1 : 1
Agitation: advantageous
Current density: 0,5 - 2 A/dm2
Bath filtration: from 10 liters
Deposition data:
Hardness: 800 - 900 HV
Layer thickness: max. 0,5 µm
Layer density: approx. 12,4 g/cm3
Form of delivery:
-Ready for use 1 g/L Rh
-Concentrate form 1 g/100ml Rh for 1 litre bath
Concentrated bath preparation:
Mix 100 ml of the Rhodium JE88 concentrate with 900 ml distilled water.