Product information "Gold Plating Bath JE250 - 3 g/L Au"
Experience the outstanding performance of our JE250 gold plating bath, ideal for depositing bright and hard gold alloy layers up to a layer thickness of 10 µm.
This weakly acidic hard gold electrolyte produces yellow, uniformly shiny hard gold coatings with high corrosion and abrasion resistance. The deposited layers consist of a robust gold/cobalt alloy that is perfect for both technical and decorative applications. The user-friendly handling and high resistance make the JE250 the ideal choice for demanding electroplating projects.
Operating data:
Gold content: 3 g/L Au
pH value: 4.0 (3.8 - 4.2)
Density: 1.035 g/ml (1.030 - 1.050)
Precipitation data:
Hardness: 150 - 220 HV
Layer thickness: Max. 10 µm
Fineness of the gold layer approx. 99.5 % Au
Working conditions:
Voltage: 2.5 - 4 V
Bath temperature: 20 - 40°C
Anode material: Platinized titanium
Anode/cathode area: approx. 1 : 1
Fabric movement: required
Current density: approx. 1 - 2.5 A/dm2
Bath filtration: from 10 liters
Deposition rate: approx. 22 mg/AMin
This weakly acidic hard gold electrolyte produces yellow, uniformly shiny hard gold coatings with high corrosion and abrasion resistance. The deposited layers consist of a robust gold/cobalt alloy that is perfect for both technical and decorative applications. The user-friendly handling and high resistance make the JE250 the ideal choice for demanding electroplating projects.
Operating data:
Gold content: 3 g/L Au
pH value: 4.0 (3.8 - 4.2)
Density: 1.035 g/ml (1.030 - 1.050)
Precipitation data:
Hardness: 150 - 220 HV
Layer thickness: Max. 10 µm
Fineness of the gold layer approx. 99.5 % Au
Working conditions:
Voltage: 2.5 - 4 V
Bath temperature: 20 - 40°C
Anode material: Platinized titanium
Anode/cathode area: approx. 1 : 1
Fabric movement: required
Current density: approx. 1 - 2.5 A/dm2
Bath filtration: from 10 liters
Deposition rate: approx. 22 mg/AMin