base metal electrolytes 

The Adhesive nickel bath JE303 enables to build up further coatings uniformly and the adhesive strength is excellent. With the JE303 very adhesive layers, especially on hard to coat materials like stainless steel, tungsten and molybdenum can be deposited. The pH value should be kept by addition or hydrochloric acid below 1.Operating data:Nickel content: 50 g/L Hydrochloric acid: 20-40 g/LOperating conditions:Voltage: 2-6 VoltBath temperature: 18°CExposition time: 30 sec.-5 min.Anodes: NickelGoods movement: not necessary at short processing timeTank material: PPHDeposition data:Nickel: 99.9 %Density: 8,9 g/cm2Special instructions:The adhesive nickel bath contains hydrochloric acid and is not suitable for light metals and tin. The bath should always be well covered as the hydrochloric acid vapors have a corrosive effect on steel and other materials.Please note that this article is a dangerous good according to the legal guidelines. For this reason we need a copy of your business registration.Therefore we kindly ask you to send us the business registration in advance.

The bright nickel bath JE300 can be used for different decorative or technical applications. It is suitable for frame and barrel plating. The bath is strongly levelling and creates an excellent brightness.Operating conditions:Voltage: 2-4 VoltBath temperature: 60 °CExposition time: approx. 2 min. (for 1 µm)Anodes: NickelCathode surface: approx. 1:1Current density: 1 - 6 A/dm²Pretreatment: Adhesive and spot-free surfaces can only be achieved on properly pretreated surfaces.Please note that this article is a dangerous good according to the legal guidelines. For this reason we need a copy of your business registration.Therefore we kindly ask you to send us the business registration in advance.

The copper bath (acid) JE540 is a universally applicable electroplating electrolyte. It is suitable for frame and barrel plating. Because of its excellent throwing power and adehesive strength the electolyte is often used as an under coat before further electroplating processes. The copper layers are fine-grained and slightly bright and create a very good adhesion between base material and final layer.Operating data:Copper content: 55 g/L (45 – 65)Sulfuric acid content: 60 g/L (55 – 75)Chloride content: 70 mg/L (50 – 100)pH-value: < 1Operating conditions:Voltage: 1,6-3 VoltCurrent density: 1 - 6 A/dm²Bath temperature: 20-30 °CExposition time: 2-15 min.Anodes: copperGoods movement: requiredBath filtration: from 10 literTank material: PPH, PP or PEDeposition data:Hardness: approx. 220 HVLayer density: 8.9 g/cm³   Please note that this article is a dangerous good according to the legal guidelines. For this reason we need a copy of your business registration.Therefore we kindly ask you to send us the business registration in advance.

The Cyanide Copper Bath JE550 is suitable for frame and barrel plating. Because of its excellent throwing power and adehesive strength the electolyte is often used as an under coat before further electroplating processes. The copper layers are fine-grained and slightly bright and create a very good adhesion between base material and final layer.Operating data:Copper: 35 g/l CuPotassium cyanide: 25-35 g/L KCN freepH-value: 11 - 12Operating conditions:Voltage: 0,5-3 VoltBath temperature: 50-60 °CExposition time: 2-15 min.Anodes: copperAnode/Cathode surface: 1 : 1 Agitation: required Current density: 1 - 3 A/dm2 Bath filtration: from 10 liters

The Matt Nickel Bath JE305 meets all requirements for a modern highperformance electrolyte. Excellent depth distribution, excellent leveling even at low nickel deposits, high ductility, good chromium ability as well as easy and problem-free bath guidance are features of the process. The matt nickel bath JE305 can be used for different decorative or technical applications. It is suitable for frame and barrel plating. Together with our JE300 bright nickel bath it is an excellent corrosion protection system.Operating conditions:Voltage: 2-4 VoltBath temperature: 60 °CExposition time: approx. 2 min. (for 1 µm)Anodes: NickelAnode-/Cathode surface: approx. 1:1Current density: 1 - 6 A/dm²Exposure time/1µm: approx. 1 mPretreatment:Bonded and spotless surfaces are only achieved on appropriately pretreated surfaces.Please note that this article is a dangerous good according to the legal guidelines. For this reason we need a copy of your business registration. Therefore we kindly ask you to send us the business registration in advance.