Product information "Platinized titanium anode 150x40 mm (2,5µm Pt)"
Suitable platinized titanium anode 150x40 mm (2,5µm Pt) for Digital V or 5 liter tanks. These anodes can be used e.g. for rhodium, platinum and gold plating baths.
The Digital V is a programmable small-size electroplating unit which can be used for all current precious metal and non precious metal processes. The machine is characterized by it's user friendliness and the easy handling.The digital display of voltage, tension and temperature guarantees a careful and secure working. The integrated timer stops processes automatically and the ampere minute counter helps to calculate the precious metal consumption. In addition to pre-installed plating programs, new programs can be installed. The machine menu is available in several european languages. Digital V has an integrated goods movement and a pen plating connection.Technical data:Dimensions (WxDxH): 820x350x260Weight: 30 kgBath volume: 4x5 l, 4x2 lBath dimensions: 190x150x220 mmRectifier: 15V/ 15ASupply voltage: 230V/ 50Hz, 120V/ 60HzOptional equipment: 2x connectable heater (2x 315W)
Titanium-fixation for anodes, 80x20 mm with screws is ideal to fixate silver, nickel or copper anodes.It is suitable for Digital V or 5 liter tanks.Dimensions:80x20 mm
The acid platinum electrolyte JE18 deposits shiny, bright and hard platinum layers. It is used for decorative as well as technical applications. The layers are highly resistant to corrosion and abrasion.Operating data:Platinum content: 2,0 g/LpH-value: <1Density: 1,08 g/ml, increasingOperating conditions:Voltage: 2 VoltBath temperature: 30 - 40 °CExposition time: 2 - 4 min.Anodes: Platinized titanium, Mixed oxideAnode/Cathode surface: 1 : 1Goods movement: requiredDeposition rate: ca. 11 mg/Amin;
Current density: ca. 0,5-1,5 A/dm2Bath filtration: from 10 litresDeposition data:Hardness: Not measurable, approx.500 HVLayer thickness: max. 1,0 µmPt content: 99,9%Form of delivery:Ready for use 2 g/L Pt
Experience the excellent quality of our JE250 gold plating bath in the 1-liter version, ideal for the deposition of bright and hard gold alloy layers up to a layer thickness of 10 µm. This weakly acidic hard gold electrolyte produces yellow, uniformly shiny hard gold coatings and offers high corrosion and abrasion resistance. The deposited layers consist of a robust gold/cobalt alloy and are suitable for both technical and decorative applications. Operating data:Gold content: 3 g/L AupH value: 4.0 (3.8 - 4.2)Density: 1.035 g/ml (1.030 - 1.050)Precipitation data:Hardness: 150 - 220 HVLayer thickness: Max. 10 µmFineness of the gold layer approx. 99.5 % AuWorking conditions:Voltage: 2.5 - 4 VBath temperature: 20 - 40°CAnode material: Platinized titaniumAnode/cathode area: approx. 1 : 1Fabric movement: requiredCurrent density: approx. 1 - 2.5 A/dm2Bath filtration: from 10 litersDeposition rate: approx. 22 mg/AMin
The JE88! GO NDG rhodium bath represents a significant innovation in electroplating technology. It is the first rhodium that is not classified as a hazardous material during transportation, allowing for safe and easy worldwide shipping.This advanced rhodium is ideal for decorative coatings in the jewelry, eyeglass frame and watch industries. It also provides effective tarnish protection for silverware. With the ability to precisely deposit layers down to 1.0 µm, the JE88! GO NDG rhodium bath ensures exceptional brilliance and durability. Its versatility makes it the ideal choice for various electroplating applications.Operating Data: Rhodium content: 0,5 g/L pH-Value: <1 Working conditions: Voltage: 2,5 – 3,5 Volt Bath temperature: 20 - 30° C Exposition time: 2 min. (1 max. 10 min) Anodes: Platiniertes Titan oder Mischoxid MOX Anode/ Cathode: 1 : 1 Current density: 0,5 – 2,0 A/dm2 Agitation: advantageous Bath filtration: from 10 Liter Deposition rate: 6 – 8mg/Amin Form of Delivery: Ready for use 0,5 g/L
The JE88! GO NDG rhodium bath offers a decisive advantage: it is the first rhodium that does not have to be declared as dangerous goods during transportation. This innovation enables problem-free and safe worldwide shipping.The revolutionary rhodium is ideal for decorative coatings with a small electroplating process in the jewelry, eyeglass frame and watch industries. It is also frequently used as effective tarnish protection for silverware. The precise deposition of layers of up to 1.0 µm enables outstanding brilliance and durability. The versatile application makes the JE88! GO NDG rhodium bath the ideal choice for various electroplating processes.Operating Data:Rhodium content: 1,0 g/LpH-Value: <1Working conditions:Voltage: 2,5 – 3,5 VoltBath temperature: 20 - 30° CExposition time: 2 min. (1 max. 10 min)Anodes: Platiniertes Titan oder Mischoxid MOXAnode/ Cathode: 1 : 1Current density: 0,5 – 2,0 A/dm2Agitation: advantageousBath filtration: from 10 LiterDeposition rate: 6 – 8mg/AminForm of Delivery:Ready for use 1,0 g/L
The JE88! GO NDG rhodium bath offers a decisive advantage: it is the first rhodium that does not have to be declared as dangerous goods during transportation. This innovation enables problem-free and safe worldwide shipping.The revolutionary rhodium is ideal for decorative coatings with a small electroplating process in the jewelry, eyeglass frame and watch industries. It is also frequently used as effective tarnish protection for silverware. The precise deposition of layers of up to 1.0 µm enables outstanding brilliance and durability. The versatile application makes the JE88! GO NDG rhodium bath the ideal choice for various electroplating processes.Operating Data:Rhodium content: 2,0 g/LpH-Value: <1Working conditions:Voltage: 2,5 – 3,5 VoltBath temperature: 20 - 30° CExposition time: 2 min. (1 max. 10 min)Anodes: Platiniertes Titan oder Mischoxid MOXAnode/ Cathode: 1 : 1Current density: 0,5 – 2,0 A/dm2Agitation: advantageousBath filtration: from 10 LiterDeposition rate: 6 – 8mg/AminForm of Delivery:Ready for use 2,0 g/L
The rhodium bath JE88-1 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 0,5 µm can be deposited.Operating data:Rhodium content: 1,0 g/L RhpH-Value: < 1Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HVLayer thickness: max. 0,5 µmLayer density: approx. 12,4 g/cm3Form of delivery:- Ready for use 1 g/L Rh- Concentrate form 1 g/100ml Rh for 1 litre bath
The rhodium bath JE88 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 1 µm can be deposited.Operating data:Rhodium content: 2,0 g/L RhpH-Value: <1Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1:1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HVLayer thickness: max. 1,0 µmLayer density: approx. 12,4 g/cm3Form of delivery:- Ready for use 2 g/L Rh- Concentrate form 2 g/100ml Rh for 1 litre bath
The rhodium bath JE88-1 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. The color of JE88 CLEAN may vary in slight nuances as the product is produced exclusively from recycled rhodium. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 0,5 µm can be deposited.Operating data:Rhodium content: 1,0 g/L RhpH-Value: <1Operating conditions:Voltage: 2-3 VoltBath temperature: 20-35°CExposition time: 2 min. (1-max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 – 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 – 900 HVLayer thickness: max. 0,5 µmLayer density: approx. 12,4 g/cm3Form of delivery:-Ready for use 1 g/L Rh-Concentrate form 1 g/100ml Rh for 1 litre bath
The rhodium bath JE88 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. The color of JE88 CLEAN may vary in slight nuances as the product is produced exclusively from recycled rhodium. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 1,0 µm can be deposited.Operating data:Rhodium content: 2,0 g/L RhpH-Value: <1Operating conditions:Voltage: 2-3 VoltBath temperature: 20-35°CExposition time: 2 min. (1-max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HVLayer thickness: max. 1,0 µmLayer density: approx. 12,4 g/cm3Form of delivery:-Ready for use 2 g/L Rh-Concentrate form 2 g/100ml Rh for 1 litre bath
The JE23GO! RS NDG black rhodium bath is an innovative development in electroplating. Its decisive advantage of not having to be declared as dangerous goods should be emphasized, which enables smooth worldwide shipping.The product is particularly suitable for decorative coatings in the jewelry and eyewear industry. It produces anthracite-black coatings with remarkable abrasion resistance, color consistency and uniformity. The black rhodium electrolyte JE23GO! RS NDG black rhodium electrolyte enables simple bath management and user-friendly handling. Precise layers of up to 0.5 µm can be deposited, which enables versatile application in various electroplating processes.Operating DataRhodium content: 2,0 g/L RhpH-Value: <1Density: 1,02 - 1,07 g/cm3Deposition DataColor, L-Value: 45 (43 - 48)Hardness: 300 - 370 HVLayer thickness: max. 0,5 μmLayer density: ca. 10,5 g/cm3Working conditionsVoltage: 2,2 - 3,5 VBath temperature: 20 °C (20 - 40°C)Exposition time: 15 min. (10 - 20 min)Anodes: Platinized titanium or mixed-metal-oxideAnode/ Cathode: 1:1Current density: 1,0 - 1,5 A/dm2Goods movement: recommendedDeposition rate: 6 - 8mg/AminBath filtration: ab 10 Liter
Form of delivery Ready for use 1 g/L
The JE23GO! RS NDG black rhodium bath is an innovative development in electroplating. Its decisive advantage of not having to be declared as dangerous goods should be emphasized, which enables smooth worldwide shipping. The product is particularly suitable for decorative coatings in the jewelry and eyewear industry. It produces anthracite-black coatings with remarkable abrasion resistance, color consistency and uniformity. The black rhodium electrolyte JE23GO! RS NDG black rhodium electrolyte enables simple bath management and user-friendly handling. Precise layers of up to 0.5 µm can be deposited, which enables versatile application in various electroplating processes.
Operating DataRhodium content: 2,0 g/L RhpH-Value: <1Density: 1,02 - 1,07 g/cm3Deposition DataColor, L-Value: 45 (43 - 48)Hardness: 300 - 370 HVLayer thickness: max. 0,5 μmLayer density: ca. 10,5 g/cm3Working conditionsVoltage: 2,2 - 3,5 VBath temperature: 20 °C (20 - 40°C)Exposition time: 15 min. (10 - 20 min)Anodes: Platinized titanium or mixed-metal-oxideAnode/ Cathode: 1:1Current density: 1,0 - 1,5 A/dm2Goods movement: recommendedDeposition rate: 6 - 8mg/AminBath filtration: ab 10 Liter
Form of deliveryReady for use 2 g/L
The black rhodium bath JE23-1 deposits dark anthracite-grey, particular decorative rhodium coatings. The layers are very abrasion resistant, colour consistent and uniform. The electrolyte is preferably used for decorative coatings in the jewellery and eyewear industry. JE23-1 is characterized by it's easy handling and usability. It works at room temperature so a time and energy intensive heating-up can be omitted. Coatings up to 0,5 µm can be deposited.
Operating Data:Rhodium content: 2,0 g/L RhpH-Value: <1Density: 1,02 – 1,07 g/cm3
Working conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 27°CExposition time: 2 min. (1 - 5 min.)Anodes: Platinized titanium, mixed-metal-oxideAnode/ Cathode: 1:1Current density: 1,0 - 1,5 A/dm2Agitation: required
Deposition rate: 6 - 8mg/AminBath filtration: ab 10 LiterDeposition Data:Hardness: 300 - 370 HVLayer thickness: max. 0,5 μmLayer density: ca. 10,5 g/cm3Form of delivery:Ready for use
Content:
1 liter
€425.26*
This website uses cookies to ensure the best experience possible. More information...